SIC Foam Ceramic Filter

Quick Details

Place of Origin:China

Type: Silicon Carbide Ceramic Plates

Application:Industrial Ceramic

Material: customizable

Processing Service:OEM

Product name:Foamed SiC in chemical

Shape:Three-dimensional network connected

Usage:Rectification

Holefraction:99%

Feature:High thermal conductivity, acid and alkali corrosion resistance

Package:Wooden Box

Hole size:0.5mm-5mm

Porosity:30%-90%

Compressive Strength:30MPa

Supply Ability

100000 Cubic Meter/Cubic Meters per Year

Packaging & Delivery

Packaging Details  Wooden Crates

Port  Shanghai ,Guagzhou ,Shenzhen,Xiamen

• Lead Time:

• Quantity(pieces)	1 - 10000	>10000
  Est. Time(days)	180	To be negotiated

Product advantages

Silicon carbide foam filter slag sheet Grey cast iron casting and copper alloy casting

With its interconnected three-dimensional structure, the foamed ceramic filter can fully reflect the four filtration mechanisms of rectification, mechanical screening, "filter cake" and adsorption when filtering molten metal. At the same time, the filter material has good chemical stability. , does not react with the alloy liquid, so as to effectively remove or reduce the inclusions in the metal liquid to improve the purity of the molten metal, so that the surface of the cast metal casting is smooth, the strength is improved, the scrap rate is reduced, and machining losses are reduced , thereby reducing energy consumption, increasing labor productivity and reducing costs.

Silicon carbide foam filter

Scope of application: suitable for ductile iron, gray iron casting and copper alloy casting

Product function:

1. Filter slag to reduce damage to castings;

2. Filter out the bubbles in the molten metal;

3. Rectification, so that the flow of molten metal is changed from turbulent to laminar flow state, reducing secondary oxidation and inhalation of molten metal, and improving the performance of castings.

Silicon carbide foam ceramic filter

1. Reduce the rejection rate of inclusion defects: reduce inclusion defects by more than 50%

2. Improve the machining performance of castings: tool life is increased by more than 30%

3. Improve the mechanical properties of castings: the mechanical properties are improved by more than 10

4. Improve the yield of the casting process: the yield of the process is increased by more than 10

Size selection: Generally recommended as follows:

Size 75mm Thickness 20~22mm,

Size 75-120mm Thickness 22~25mm,

Size 120-150mm Thickness 25~30mm,

Size>150mm Thickness 30~40mm